Attributs du produit

Modèle: 47F165 47F180 47F200 47F210 47F240

marque: Houming

La Norme: ASTM, AiSi

Si Alliage: Est l'alliage

Tolérance: ± 1%

Service De Traitement: Pliant, Soudage, Décollage, Perforation, Coupe

Processing Service: Bending Welding Decoiling

Standard: ASTM

Capacité d'approvisionnement et informa...

transport: Ocean,Land

Lieu d'origine: Chine

Hafen: Qingdao,Shanghai,Tianjin

Type de paiement: L/C,T/T,D/P,D/A

Incoterm: FOB,CFR,CIF,EXW

Emballage & livraison

Unités de vente:

Metric Ton

ASTM non orienté 47F Silicon en acier en acier

0.47 mm (0.0185 in.) Thickness
Core-Loss Type	Maximum Core Loss,
Core-Loss Type	W/kg_	(W/b)
47F165	3.64	(1.65)
47F180	3.97	(1.80)
47F190	4.19	(1.90)
47F200	4.41	(2.00)
47F210	4.63	(2.10)
47F240	5.29	(2.40)
47F280	6.17	(2.80)
47F400	8.82	(4.00)
47F450	9.92	(4.50)

Comparaison de bobine en acier en silicium

Bobine en acier roulé à froid

Avantages:

L'acier en silicium non orienté a des propriétés magnétiques isotropes, une perte de fer relativement faible, une bonne machinabilité et des performances de coût de matériau relativement élevées. Ces avantages rendent l'acier en silicium largement utilisé dans les moteurs, les générateurs et les petits transformateurs.

Désavantages:

L'acier en silicium non orienté a des propriétés magnétiques inférieures à l'acier au silicium orienté, a une perte de courant de Foucault plus élevée, et les restrictions d'épaisseur peuvent affecter la conception et les performances de l'équipement d'alimentation à haute efficacité fabriqué par certaines usines.

Après avoir comparé ces deux aciers au silicium, en termes de performances de coût, l'acier en silicium non orienté peut être plus adapté aux équipements électriques qui nécessitent des propriétés magnétiques uniformes, mais dans les applications à haute efficacité et à faibles exigences de perte, il est recommandé que les clients puissent Besoin de considérer l'acier au silicium orienté.

Précautions pour l'application de l'acier en silicium non orienté

Lorsque vous utilisez des bobines en acier électrique non orientées (NOES) pour fabriquer certains équipements électriques, nous devrons peut-être prêter attention aux problèmes clés suivants pour assurer les meilleures performances et la meilleure durée de vie de l'équipement.

Non-Oriented Electrical Steel Fully Processed (FP) ASTM A677
ASTM Type	Core Loss by Thickness		Typical Electrical Resistivity Microhm-CM	Some Characteristics	Typical Applications
	Watts/lb 15 Kilogausses 60HZ
	Thick	Max w/lb
47F165	0.185	1.65	45-55	Low core loss, good permeability at low and intermediate inductions.	High-reactance cores, generators, stators of highefficiency rotating equipment.
47F180	0.185	1.80	45-55	Low core loss, good permeability at low and intermediate inductions.	High-reactance cores, generators, stators of highefficiency rotating equipment.
47F190	0.185	1.90	45-55	Low core Toss, good permeability at low and intermediate inductions.	generators, stators Of highefficiency rotating equipment and relays.
47F200	0.185	2.00	40-50	Good core loss, good permeability at all inductions and low exciting current, good stamping properties.	Small generators, highefficiency, continuous duty rotating A-C and D-C machines and transformers.
47F210	0.185	2.10	35-45	Good core loss, good permeability at all inductions and low exciting current, good stamping properties.	Small generators, highefficiency, continuous duty rotating A-C and D-C machines and transformers.
47F240	0.185	2.40	35-45	Good stamping properties. Good permeability at high flux densities.	Small motors, generators, ballasts, and relays.
47F280	0.185	2.80	20-30	Good stamping properties. Good permeability at high flux densities.	Small motors, generators, ballasts, and relays.

1. Sélectionnez le matériau et les spécifications de la plaque d'acier

Nous devons sélectionner le grade en acier en silicium le plus approprié et le niveau correspondant. Différentes classes en acier en silicium et grades de bobine en acier ont différentes propriétés magnétiques et mécaniques. Le grade en acier en silicium approprié doit être sélectionné en fonction des exigences spécifiques de l'équipement.

Dans le même temps, les clients doivent également considérer l'épaisseur du matériau: plus l'épaisseur est mince, plus la perte de courant de Foucault, mais la difficulté de traitement et le coût augmentent également en conséquence. Par conséquent, un équilibre doit être trouvé entre les performances et les coûts.

2. Traitement en profondeur et traitement des bobines en acier lamelle à froid

(1) Processus d'estampage: Lors de l'estampillation des feuilles d'acier en silicium dans l'usine, les techniciens doivent utiliser des équipements d'estampage et des moules précis pour assurer la précision de traitement et la qualité de surface de l'acier en silicium. Il s'agit de garantir que les bavures et les microfissures doivent être évités pendant le processus d'estampage.

(2) Processus de laminage: La stratification est également un processus clé dans la fabrication du noyau en acier du silicium. L'usine doit s'assurer que la stratification est serrée et uniforme pendant le traitement, ce qui réduira les lacunes et les pertes.

(3) Revêtement d'isolation: la surface des feuilles d'acier en silicium est généralement enduit d'une couche d'isolation pour réduire les pertes de courant de Foucault. Pendant le traitement et l'assemblage, les dommages à la couche d'isolation doivent être évités.